The Effect of Mineral Pigments on Mechanical Properties of Concrete

Abstract

 Pigmented concrete exhibits artesian properties in addition to ordinary concrete properties, explicitly high strength, excellent durability, and weather resistance. However, the influence of several parameters that affect the characteristics of colored concrete should be studied; extensively. In this paper, the impact of the w/b (water/binder) ratio using color pigments on the mechanical properties such as compressive and flexural strengths of colored cement mortar prisms and cubes experimentally investigated. The experimental program included 21 mixes with six cubes and three flexural prisms specimens for assessing compressive and flexural strength, respectively. The blends included different water/binder ratios with values of 0.4, 0.5, and 0.6, in addition to several color pigments as a partial replacement of cement. The percentage of replacements altered between 0, 2.5%, 5% and 7.5% with two different shades of pigments consisting of red iron and green chromium oxide. Based on the experimental results, empirical expressions were generated based on Abram’s law to assess the relationship between the compressive strength of colored concrete and w/b ratio. The results revealed that the compressive and flexural strength of colored concrete is influenced by w/b ratio and partially replacement percentage of cement by color pigment not proportionally direct. Furthermore, the shade of pigments also has a different impact as well.